牌號(hào) 615
美國(guó)UNS S41800
對(duì)應(yīng)標(biāo)準(zhǔn) ASTM A565/A565M-2010(R2017)
高溫用馬氏體不銹鋼棒
Martensitic Stainless Steel Bars for High-Temperature Service
歸類(lèi) 馬氏體不銹鋼
615 化學(xué)元素成分含量(%)
成分 C Si Mn P S Cr Ni Mo W
最小值 0.15 - - - - 12 1.8 - 2.5
最大值 0.2 0.5 0.5 0.04 0.03 14 2.2 0.5 3.5
碳當(dāng)量計(jì)算
615 機(jī)械性能
條件 抗拉強(qiáng)度
σb
Mpa 		屈服點(diǎn)
σs
Mpa 		斷后伸長(zhǎng)率或延伸率
δ
% 		斷面收縮率
ψ
% 		硬度
HBW
HT - Heat treated (for high-temperature service) ≥965 ≥760 ≥15 ≥45 302~352
退火 ≤311
① HT - Heat treated (for high-temperature service)：1800 to 1850°F [980 to 1010°C], quench in air or oil and double temper at 1150°F (620°C] min for 2 h min for each tempering treatment.